Wiendartun, Jaenudin Kamal, Dadi Rusdiana, Andhy Setiawan, Dani Gustaman Syarief
A study on the effect of heat treatment condition on the characteristics of MnO2 added-Fe2TiO5 ceramics for NTC thermistor has been carried out. The ceramics were produced by pressing an homogenous mixture of Fe2O3 (local/ yarosite), TiO2 and MnO2 (2.0 mole %) powders in appropriate proportions to produce Fe2TiO5 based ceramics and sintering the pressed powder at 1050 ºC for 3 hours in oxygen gas. Some sintered pellets were heat treated by heating them at 300 ºC for 5, 15 and 25 minutes in Ar + 7% H2 gas. The XRD analyses showed that the Fe2TiO5 ceramics with and without heat treatment time had orthorhombic structure. No peak from second phase was observed from the XRD profiles. From the electrical characteristics data, it was known that the heat treatment could change the electrical characteristics of the Fe2TiO5 based-thermistor. The thermistor constant (B) and room temperature resistivity (ρRT) decreased with the increasing of heat treatment time. All ceramics made had thermistor characteristics namely B = 3459-7596 K and ρRT = 1.056-6936.062 MΩcm. Thermistor constant of the ceramics was relatively big, indicated that ceramics made from local iron oxide in this work fit the market requirement for NTC thermistor. © 2018 Trans Tech Publications, Switzerland.
Department of Physics Education, Indonesia University of Education (UPI), Bandung, 40154, Indonesia; PSTNT-BATAN, Jl. Tamansari 71, Bandung, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock