H. Aliah, B. Bernando, F. Puspitasari, A. Setiawan, P. Pitriana, B.W. Nuryadin, M.A. Ramdhani
This research aims to examine the influence of the composition of TiO2 and ZnO as the working electrode on the efficiency of DSSC. The working electrode is prepared by depositing TiO2 and ZnO pastes on top of the FTO glass using the doctor blade method. The samples were then heated in an oven at a temperature of 250 ° C for 4 hours. In this study, three TiO2 / ZnO compositions were prepared and assembled into DSSC components with red spinach dye. SEM image shows that the composition of TiO2 / ZnO (0:2) produces the best surface morphology that is indicated by the number and aggregate uniform pores. This is consistent with the results of testing the electrical properties of the sample. The solar cell with the working electrode composed of TiO2 / ZnO (0: 2) yields an efficiency of 0.0515%, higher than the composition (2: 0) and (1: 1) which respectively yields 0.0044% and 0.0015%. © Published under licence by IOP Publishing Ltd.
Physics Department, UIN Sunan Gunung Djati, Jl. A.H Nasution 105, Bandung, Indonesia; Faculty of Mathematics and Natural Science, Universitas Pendidikan Indonesia, Jl. Dr. Setiabudhi 229, Bandung, Indonesia; Physics Education Program, UIN Sunan Gunung Djati, Jl. A.H Nasution 105, Bandung, Indonesia; Informatics Department, UIN Sunan Gunung Djati, Jl. A.H Nasution 105, Bandung, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock